Product characteristics
This series is made of functional group grafted modified polyolefin, which can undergo esterification reaction withhydroxyl groups in wood powder to reduce the polarity of wood powder and make it compatible with resin; Thus, thetensile strength and elastic modulus of wood plastic products can be improved, the water absorption rate of woodplastic products can be reduced, and the strength can be maintained for a long time.
| Physical property index | Testing method | unit | TG919B | TG901B |
| Melt index [1] | ASTM D1238 | g/10min | 1.5 - 2.5 | 30 - 50 |
| Group content [2] | TZ/GA2023 - 1 | MAH wt% | Very high | tall |
| matrix resin | - | - | PE | PP |
Note: [1] ASTM D1238:190C, 2.16kg. [2] Medium: 0.6wt% -0.8wt%; High: 0.8wt% -1.0wt%; Very high>1.0wt%
| model | DESCRIPTION |
| TG919B | High performance wood plastic compatibilizer. Used as a compatibilizer for bamboo wood powder/fiber filled PE composite materials, it can effectively improve the interfacial compatibility between PE and fillers, and promote the uniform dispersion of fillers. Typical application for PE wood plastic composite materials, recommended addition amount is 2-5%. |
| TG901B | Used as a compatibilizer for bamboo wood powder/fiber filled PP composite materials, it can effectively improve the interfacial compatibility between PP and fillers, and promote the uniform dispersion of fillers. Typical application for PP wood plastic composite materials, recommended addition amount is 2-5%. |
Attention: The above data are typical laboratory values, true and reliable, for reference only, and do not make formal quality commitments.